Solution for dozer electrophoresis paint
Product Introduction
HL-1605LB/HL-1530G Black Cationic Epoxy Electrocoat for auto is a
new generation electrophoretic coating researched and developed by
HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic
coatingthat isenvironment-friendly withhigh propertyandlow cost.
Such coatingdoesnot contain heavy metal like lead, tin, cadmium and
mercury etc.
It is a two-component, water-dispersed resin,meanwhile, it took in
features of previous products, andcan adapt galvanized steel sheet
perfectly,almost canbe applied to foundation coating of all metal
suchas: cold and hot rolled steel sheet, galvanized steel sheet,
aluminum products, zinc-aluminum alloy sheet and stainless steel
sheetetc
This product features shown below :
The appearance of the coating is flat,delicate,smooth.
|
The bath has strong anti-shrink age and anti-pollution ability
|
Coating fullness of good,better substrate hiding.
|
The main component Matrix resin :
Neutralizing agent: organic acid
| Solvent: alcohol ether |
Pigment: carbon black, kaolin, antirust pigment
| Curing agent: Fully enclosed multi isocyanate |
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 1000.00-1500.00
Paste 250.00
DI water 2000.00-2800.00
Total 3250.00-4550.00
⑵ Ripening conditions
Sample quantity: 3000～5000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-35℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(175-185)℃×(20-30)min (Keeping temperature of
parts coated)
Bath on site management project :
Good bath data and coating quality, from the strict parameters
management and maintenance of equipment, production line according
to its own reality time situation, can have different management
project and specifications, recommend the construction parameters
see the table below for reference:
| Classification | Project | Control Data | Testing frequency |
| New bath | Anolyte |
| Electrophoresis tank | Ratio | 1:(4-6) | -- | |
| Ripening time | 24-48 | -- | |
| Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day |
| PH | 5.7-6.0 | 2.0-3.5 | once a day |
| Conductivity ( μs/cm ) | 1200±400 | 1500±700 | once a day |
| P/B | 0.08-0.15 | once a week |
| L panel | Smooth horizontal plane and vertical plane without obvious
differences | once a week |
| Solvent content (%) | 0.5-1.8 | once a week |
| Liquid level Fall head (cm ) | 10-15 | once a day |
| ED voltage( V ) | 0-300 | once a day |
| Break voltage ( V ) | ≥320 | once a week |
| Bath temperature ( ℃ ) | 28-35 | once a day |
| ED time( S ) | 60-180 | once a day |
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day |
| Baking furnace | Provisions furnace temperature( ℃ ) | 180-190 | once a day |
| Curing conditions | Drying temperature |
(175-185)℃×(20-30)min (With content holding time) | once a day |
Construction equipment :
Cathodic electrophoretic coating construction in the
electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
| Circulation devices (including filter, fill the paint device) |
DI water equipment
| DC power supply and the power supply unit |
Anode box (tube) and circulation device
| Ultrafiltration device |
Cleaning devices
| Heat exchanging equipment |
Curing device
|
Storage, packaging and transportation :
This product is a water-borne industrial coatings, non-hazardous,
non-inflammable and explosive products; transportation to prevent
direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L
Plastic barrel; in the transport and storage of drums should be
maintained clean, avoid charging the dirt brought in on drums
during filling tank, again checked and confirmed that the quality
of products, including paste resin, emulsions and additives should
be indoor storage, good ventilation, dry, protect against freezing
and overheating, the storage temperature should be controlled at
5～35℃, products from the date of production, over shelf,
experimentation is required to determine whether can continue to
use.