Solution for the bus electrophoresis paint
Product Introduction
HLS-5701LB/HLS-5750 Gray Cationic Epoxy Electrocoat for auto is the
7th generation electrophoretic coating researched and developed by
HLS Paint (Shanghai) Co., Ltd. in cooperation with Germany HS
International Chemical Industry Group. It represents modern
technology of cathodic electrophoretic coating that is
environment-friendly with high property and low cost. Such coating
does not contain heavy metal like lead, tin, cadmium and mercury
etc. It is a two-component, water-dispersed resin,meanwhile, it
took in features of previous products, and can adapt galvanized
steel sheet perfectly, almost can be applied to foundation coating
of all metal, such as: cold and hot rolled steel sheet, galvanized
steel sheet, aluminum products, zinc-aluminum alloy sheet and
stainless steel sheet etc.
This product features shown below:
| Good stability of bath can adaptable for a longer updating cycle | High throwing power, internal and external uniformity. | Suitable for automotive, cab, car, bus, truck, trailer and so on. |
Main ingredients
| Pigment: carbon black, kaolin, antirust pigment | Solvent: alcohol ether |
| Additives: surface active agent, prevent shrinkage cavity agent |
The main supplier
| Material name | Supplier |
| Bisphenol A epoxy resins | Formosa Plastic Group / Kukdo / Dow Chemical |
| Polyisocyanates | Bayer |
| Amine hardendner | INTERSCAN / Huntsman Corporation |
Bath on site management project
Good bath data and coating quality, from the strict parameters
management and maintenance of equipment, production line according
to its own reality time situation, can have different management
project and specifications, recommend the construction parameters
see the table below for reference:
| Classification | Project | Control Data | Testing frequency |
| New bath | Anolyte |
| Electrophoresis tank | Ratio | 1:4 | -- | |
| Ripening time | 24-48 | -- | |
| Solid ( 120 ℃ /1h ,% ) | 18±2 | -- | once a day |
| PH | 5.8-6.2 | 2.0-3.5 | once a day |
| Conductivity ( μs/cm ) | 1200±400 | 2000±1000 | once a day |
| P/B | 0.25-0.39 | once a week |
| Throwing power (Four-box method), ≥ | 50% | once a year |
| Solvent content (%) | 0.8-1.5 | once a week |
| Liquid level Fall head (cm ) | 10-15 | once a day |
| ED voltage( V ) | 0-300 | once a day |
| Break voltage ( V ) | ≥350 | once a week |
| Bath temperature ( ℃ ) | 30±2 | once a day |
| ED time( S ) | 60~180 | once a day |
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day |
| Baking furnace | Provisions furnace temperature( ℃ ) | 180-200 | once a day |
| Curing conditions | Drying temperature |
(170-180) ×( ℃ 15-20)min (With content holding time) | once a day |