Solution for application of electrophoresis paint of fertilizer
machine
Product Introduction :
HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is
a new generation electrophoretic coating researched and developed
by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating
that is environment-friendly with high property and low cost. Such
coating does not contain heavy metal like lead, tin, cadmium and
mercury etc. It is a two-component, water-dispersed
resin,meanwhile, it took in features of previous products, and can
adapt galvanized steel sheet perfectly, almost can be applied to
foundation coating of all metal
such as: cold and hot rolled steel sheet, galvanized steel sheet,
aluminum products and stainless steel sheet etc.
This product features shown below :
1, Good stability of bath can adaptable for a longer updating
cycle.
2, Coating fullness of good, better substrate hiding .
3, Strong anti-corrosion properties, good salt spray resistance
workpiece edge.
Main ingredients :
Pigment: Titanium pigment, carbon black, kaolin, antirust pigment
| Additives: surface active agent, prevent shrinkage cavity agent |
Solvent: alcohol ether
| Neutralizing agent: organic acid |
Curing agent: totally enclosed multi-isocyanates
| Matrix resin: polyurethane modified epoxy resin |
Bath on site management project:
Good bath data and coating quality, from the strict parameters
management and maintenance of equipment, production line according
to its own reality time situation, can have different management
project and specifications, recommend the construction parameters
see the table below for reference:
| Classification | Project | Control Data | Testing frequency |
| New bath | Anolyte |
| Electrophoresis tank | Ratio | 1:6 | -- | |
| Ripening time | 24-48 | -- | |
| Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day |
| PH | 5.6-6.2 | 2.0-3.5 | once a day |
| Conductivity ( μs/cm ) | 1200±400 | 2000±1000 | once a day |
| P/B | 0.08-0.15 | once a week |
| Solvent content (%) | 0.5-1.2 | once a week |
| Liquid level Fall head (cm ) | 10-15 | once a day |
| ED voltage( V ) | 0-300 | once a day |
| Break voltage ( V ) | ≥320 | once a week |
| Bath temperature ( ℃ ) | 30-36 | once a day |
| ED time( S ) | 60~180 | once a day |
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day |
| Baking furnace | Provisions furnace temperature( ℃ ) | 185-195 | once a day |
| Curing conditions | Drying temperature |
(180-190) ℃ ×(15-20)min (With content holding time) | once a day |