High throwing power penetration electrophoresis paint for
engineering machinery
Product Introduction:
HS-6060LB/HS-2516G Gray Cationic Epoxy Electrocoat for auto is a
new generation electrophoretic coating researched and developed by
HLS Paint (Shanghai) Co., Ltd.
|
It represents modern technology of cathodic electrophoretic coating
that is environment-friendly with high property and low cost. Such
coating does not contain heavy metal like lead, tin, cadmium and
mercury etc. It is a two-component, water-dispersed
resin,meanwhile, it took in features of previous products, and can
adapt galvanized steel sheet perfectly, almost can be applied to
foundation coating of all metal
|
such as: cold and hot rolled steel sheet, galvanized steel sheet,
aluminum products, zinc-aluminum alloy sheet and stainless steel
sheet etc.
|
This product features shown below:
1,The bath has strong anti-shrinkage and anti-pollution ability.
2,Good stability of bath can adaptable for a longer updating cycle.
3,Coating fullness of good, better substrate hiding .
4,Excellent leveling coating,good bonding force and compatibility
with plastic powder.
The main component Matrix resin :
Matrix resin:polyurethane modified epoxy resin
|
Curing agent:totally enclosed multi-isocyanates
|
Additives: surface active agent, prevent shrinkage cavity agent
|
Product quality data :
| Project | Technical data | Test standard |
Resin
(HS-6060LB) | Gray Paste (HS-2516G) |
| Appearance | —— | Milky white liquid | Gray viscous liquid,no agglomeration | Visual |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±400 | —— | HG/T 3334 |
| Storage stability |
No stratified state, and there were no obvious difference compared
to before storage | In 5-35 ℃ temperature 1 year |
Note: pH, conductivity measurement in the resin/pure water = 1:1
dilution
Bath on site management project:
Good bath data and coating quality, from the strict parameters
management and maintenance of equipment, production line according
to its own reality time situation, can have different management
project and specifications, recommend the construction parameters
see the table below for reference:
| Classification | Project | Control Data | Testing frequency |
| New bath | Anolyte |
| Electrophoresis tank | Ratio | 1:(3.5-4.5) | -- | -- |
| Ripening time | 24-48 | -- | -- |
| Solid ( 120 ℃ /1h ,% ) | 14±4 | -- | once a day |
| PH | 5.7-6.2 | 2.0-3.5 | once a day |
| Conductivity ( μs/cm ) | 1200±400 | 1500±500 | once a day |
| P/B | 0.20-0.30 | once a week |
| L panel | Smooth horizontal plane and vertical plane without obvious
differences | once a week |
| Solvent content (%) | 0.5-1.8 | once a week |
| Liquid level Fall head (cm ) | 10-15 | once a day |
| ED voltage( V ) | 0-300 | once a day |
| Break voltage ( V ) | ≥320 | once a week |
| Bath temperature ( ℃ ) | 30-36 | once a day |
| ED time( S ) | 60-180 | once a day |
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day |
| Baking furnace | Provisions furnace temperature( ℃ ) | 170-185 | once a day |
| Curing conditions | Drying temperature |
(165-180)℃×(20-30)min (With content holding time) | once a day |
Specification statement :
This manual contains information and recommendations are based on
our current knowledge and experience, accurate to the date of
publication so far. It cannot be used as a guarantee or commitment,
in any case, responsibility for users to decide on the use of this
product is intended availability. We remain in the process or new
development within the scope of the right to change product
specifications. Because we cannot control the construction
conditions, hope through customers own experiments to determine
satisfaction with the final results.
If you want to learn more about HLS coating products, please
contact Sales Department of Shanghai HLS now