Low temperature curing electrophoresis paint for auto parts
Product Introduction :
OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy
Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation
of independent research and development of electrophoretic coating.
The lead, cadmium, chromium, mercury and other heavy metals,
two-component aqueous dispersion resin. At the same time, inherited
the characteristics of several generations of product quality,
OHT-825 on galvanized steel sheet has good adaptability, almost at
the bottom of all the metal material coating
such as: cold rolled steel, galvanized steel, aluminum, stainless
steel plate, rubber parts, zinc and aluminum alloy plate, such as
applicable.
This product features shown below:
Good stability of bath can adaptable for a longer updating cycle.
|
The bath has strong anti-shrinkage and anti-pollution ability. |
High penetration and good uniformity of internal and external.
|
Particularly suitable for high temperature baking of the workpiece,
in particular, rubber and metal binding parts and zinc aluminum
alloy material.
|
Main ingredients:
Curing agent: Modified low temperature curing agent
| Neutralizing agent: organic acid |
Solvent: alcohol ether
| Pigment: carbon black, kaolin, antirust pigment |
Product film performance :
| Project | | Indicator | Test standard |
| Appearance | Normal / Abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm,≥ | 7 | GB/T 9753 |
| Adhesion | level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | Kg.cm | 50 | GB/T 1732 |
| Gloss | 60° | 60-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃ ≥ | 240 | GB/T 1733 |
| Acid resistance | h(0.05N H2SO4) ≥ | 48 | GB/T 9274 |
| Alkali resistance | h(0.1N NaOH) ≥ | 48 | GB/T 9274 |
| *Salt spray resistance | film thickness ≥ 20μm | 800 | JIS K 5600-7-1 |
* Note: The substrate use the Bonder standard phosphating steel
panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Specification statement :
This manual contains information and recommendations are based on
our current knowledge and experience, accurate to the date of
publication so far. It cannot be used as a guarantee or commitment,
in any case, responsibility for users to decide on the use of this
product is intended availability. We remain in the process or new
development within the scope of the right to change product
specifications. Because we cannot control the construction
conditions, hope through customers own experiments to determine
satisfaction with the final results.
If you want to learn more about HLS coating products, please
contact Sales Department of Shanghai HLS now