Special furniture white electrophoresis paint
Product Introduction :
| HS-5500LB/HS-5500 White epoxy acrylic cathodic electrophoretic
coating for auto is the 8th generation electrophoretic coating
researched and developed by HLS Paint (Shanghai) Co., Ltd. and get
the national invention patent and the Shanghai science and
technology commission of high-tech transformation project. |
| It represents modern technology of cathodic electrophoretic coating
that is environment-friendly with high property and low cost. Such
coating does not contain heavy metal like lead, tin, cadmium and
mercury etc. It is a two-component, water-dispersed resin. The
coating that does not contain tin element meet the latest
environ-mental regulations of European Union, North America, Japan
and other requirements in advance, which is the inevitable trend of
future environ-mental coating and low cost; meanwhile, it took in
features of previous products, and can adapt galvanized steel sheet
perfectly, almost can be applied to foundation coating of all
metal, |
| such as: cold and hot rolled steel sheet, galvanized steel sheet,
aluminum products, zinc-aluminum alloy sheet and stainless steel
sheet etc. |
This product features shown below:
The appearance of the coating is flat, delicate, smooth, and has a
good hiding power for the substrate
| Good stability of bath can adaptable for a longer updating cycle. | The bath has strong anti-shrinkage and anti-pollution ability. |
Main ingredients:
①,Neutralizing agent: organic acid
②,Pigment: titanium dioxide, kaolin,antirust pigment
③,Additives: surface active agent, prevent shrinkage cavity
agent,resistance to yellowing agen
Product film performance :
| Project | Indicator | Test standard |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 24 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 600 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel
panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Construction equipment
Cathodic electrophoretic coating construction in the
electrophoresis tank, so need to have the following equipment:
Electrophoresis tank
Circulation devices (including filter, fill the paint device)
DI water equipment
DC power supply and the power supply unit
Anode box (tube) and circulation device
Ultrafiltration device
Cleaning devices
Heat exchanging equipment
Curing device
Specification statement :
This manual contains information and recommendations are based on
our current knowledge and experience, accurate to the date of
publication so far. It cannot be used as a guarantee or commitment,
in any case, responsibility for users to decide on the use of this
product is intended availability. We remain in the process or new
development within the scope of the right to change product
specifications. Because we cannot control the construction
conditions, hope through customers own experiments to determine
satisfaction with the final results.